VALOX 830 is a 30% glass fibre reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
美國(guó)Sabic沙伯基礎(chǔ)創(chuàng)新塑料:PBT 830、855、865、DR48、DR48 - CS1049、DR51、ENH3500、ENH4530、ENH4550、ENH4560、ENH4565、HX312C、HX420HP、K3501、K4530、K4560、SHF4910、SHF4930、SHF4960、V2000DM、V3500EX、V4860HR、VX4920、VX4930、VX5011、VX5022、
VALOX ? Resin 830
SI
| British
| Metric
| PDF
Europe-Africa-Middle East: COMMERCIAL
VALOX 830 is a 30% glass fibre reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 5 mm/min
1420
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
1420
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
3
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
3
%
ASTM D 638
Tensile Modulus, 5 mm/min
107000
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
2090
kgf/cm2
ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span
2090
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
75400
kgf/cm2
ASTM D 790
Taber Abrasion, CS-17, 1 kg
30
mg/1000cy
SABIC Method
Tensile Stress, yield, 5 mm/min
140
MPa
ISO 527
Tensile Stress, break, 5 mm/min
140
MPa
ISO 527
Tensile Strain, yield, 5 mm/min
3
%
ISO 527
Tensile Strain, break, 5 mm/min
3
%
ISO 527
Tensile Modulus, 1 mm/min
10500
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
215
MPa
ISO 178
Flexural Stress, break, 2 mm/min
200
MPa
ISO 178
Flexural Strain, break, 2 mm/min
3
%
ISO 178
Flexural Modulus, 2 mm/min
8800
MPa
ISO 178
Hardness, H358/30
174
MPa
ISO 2039-1
Hardness, Rockwell R
123
-
ISO 2039-2
IMPACT
Value
Unit
Standard
Charpy Impact, unnotched, 23°C
60
kJ/m2
ISO 179/2C
Charpy Impact, unnotched, -30°C
55
kJ/m2
ISO 179/2C
Izod Impact, unnotched, 23°C
81
cm-kgf/cm
ASTM D 4812
Izod Impact, unnotched, -30°C
81
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
9
cm-kgf/cm
ASTM D 256
Izod Impact, notched, 0°C
9
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
9
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
35
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
50
kJ/m2
ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
50
kJ/m2
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
10
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 0°C
9
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
9
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
9
kJ/m2
ISO 179/1eA
Charpy Impact, notched, 23°C
10
kJ/m2
ISO 179/2C
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
9
kJ/m2
ISO 179/1eA
Charpy Impact, notched, -30°C
10
kJ/m2
ISO 179/2C
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
60
kJ/m2
ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
50
kJ/m2
ISO 179/1eU
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate A/50
220
°C
ASTM D 1525
Vicat Softening Temp, Rate B/50
208
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
220
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
200
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
208
°C
ASTM D 648
CTE, -40°C to 40°C, flow
2.7E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.8E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
1.97E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
6.59E-05
1/°C
ISO 11359-2
CTE, 23°C to 80°C, flow
2.5E-05
1/°C
ISO 11359-2
CTE, 23°C to 80°C, xflow
8.1E-05
1/°C
ISO 11359-2
CTE, 23°C to 150°C, flow
1.51E-05
1/°C
ISO 11359-2
CTE, 23°C to 150°C, xflow
1.42E-04
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate A/50
220
°C
ISO 306
Vicat Softening Temp, Rate B/50
208
°C
ISO 306
Vicat Softening Temp, Rate B/120
208
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
220
°C
ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
202
°C
ISO 75/Ae
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
220
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
200
°C
ISO 75/Af
Relative Temp Index, Elec
120
°C
UL 746B
Relative Temp Index, Mech w/o impact
120
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.55
-
ASTM D 792
Filler Content
30
%
ASTM D 229
Mold Shrinkage on Tensile Bar, flow (2) (5)
0.4 - 0.8
%
SABIC Method
Mold Shrinkage, flow, 3.2 mm (5)
0.2 - 1
%
SABIC Method
Mold Shrinkage on Tensile Bar, xflow (2) (5)
0.6 - 1
%
SABIC Method
Melt Flow Rate, 265°C/2.16kgf
16
g/10 min
ASTM D 1238
Melt Flow Rate, 265°C/5.0 kgf
45
g/10 min
ASTM D 1238
Density
1.55
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.15
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.06
%
ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg
23
cm3/10 min
ISO 1133
Melt Volume Rate, MVR at 265°C/2.16 kg
14
cm3/10 min
ISO 1133
Melt Volume Rate, MVR at 265°C/5.0 kg
35
cm3/10 min
ISO 1133
Melt Viscosity, 260°C, 1500 sec-1
208
Pa-s
ISO 11443
ELECTRICAL
Value
Unit
Standard
Volume Resistivity
>1.E+15
Ohm-cm
ASTM D 257
Dielectric Strength, in oil, 0.8 mm
27
kV/mm
ASTM D 149
Dielectric Strength, in oil, 1.6 mm
23
kV/mm
ASTM D 149
Dielectric Strength, in oil, 3.2 mm
15
kV/mm
ASTM D 149
Relative Permittivity, 1 MHz
3.2
-
ASTM D 150
Dissipation Factor, 1 MHz
0.013
-
ASTM D 150
Arc Resistance, Tungsten {PLC}
6
PLC Code
ASTM D 495
Hot Wire Ignition {PLC)
0
PLC Code
UL 746A
High Voltage Arc Track Rate {PLC}
2
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
3
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A
Volume Resistivity
>1.E+15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil, 0.8 mm
27
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 1.6 mm
23
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 3.2 mm
15
kV/mm
IEC 60243-1
Relative Permittivity, 100 Hz
3.6
-
IEC 60250
Relative Permittivity, 1 MHz
3.2
-
IEC 60250
Dissipation Factor, 50/60 Hz
0
-
IEC 60250
Dissipation Factor, 100 Hz
0.002
-
IEC 60250
Dissipation Factor, 1 MHz
0.013
-
IEC 60250
Comparative Tracking Index
325
V
IEC 60112
Comparative Tracking Index, M
150
V
IEC 60112
Relative Permittivity, 50/60 Hz
3.3
-
IEC 60250
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94HB Flame Class Rating (3)
1.5
mm
UL 94
UL Recognized, 94HB Flame Class Rating 2nd value (3)
3
mm
UL 94
Glow Wire Flammability Index 750°C, passes at
1
mm
IEC 60695-2-12
Source GMD, last updated:2012/06/18
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
110 - 120
°C
Drying Time
4 - 6
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
260 - 285
°C
Nozzle Temperature
265 - 275
°C
Front - Zone 3 Temperature
260 - 280
°C
Middle - Zone 2 Temperature
255 - 280
°C
Rear - Zone 1 Temperature
240 - 260
°C
Hopper Temperature
40 - 60
°C
Mold Temperature
60 - 110
°C
Source GMD, last updated:2012/06/18